Sustainable Graphene-like Carbon from Ghars Date Waste for Photothermal-Enhanced Solar Desalination: A Circular Economy Approach

The valorization of agricultural waste into high-value carbon nanomaterials offers dual benefits: it reduces pollution and provides low-cost materials for sustainable technologies. This work synthesizes graphene-like carbon from Ghars date waste via mild KOH-assisted pyrolysis at 1000 °C. The material (G-GhW1000) exhibits a sharp (002) XRD peak at 26.16° (d-spacing = 3.40 Å), a characteristic π → π* transition at 253 nm, and a high C/O ratio of 27.37. Dispersed in tap water (0.5 g/L) by simple hand shaking (without ultrasonication), it serves as a photothermal nanofluid in a modified single-slope solar still (MSS). Under outdoor conditions, the MSS produces 4.69 L·m−2·day−1, which is 18.7% higher than a conventional still, with thermal efficiency rising from 27.2% to 30.8% (with a reproducible 19.0% enhancement in summer). Samples prepared at 800 °C and 900 °C give 4.0% and 6.4% lower yields, while the 1100 °C sample gives only 6.0% improvement, confirming 1000 °C as the optimal temperature. The superior performance at 1000 °C is attributed to the optimal balance between graphitization, deoxygenation, and structural integrity, as evidenced by XRD, FTIR, EDX and UV-Vis analyses. The enhanced performance is linked to higher water temperature (68 °C) and larger ΔT. The distilled water meets WHO standards (TDS 9.35 mg/L, >99.4% reduction) with no detectable graphene-like carbon carryover. This work demonstrates the potential of waste-derived graphene-like carbon as a low-cost additive for solar desalination, addressing water scarcity and waste management within a circular economy framework. To our knowledge, this is the first study to use Ghars date waste-derived graphene-like carbon in a solar still.