Research Advances in the Corrosion Behavior and Underlying Mechanisms of Additively Manufactured Titanium Alloys

Titanium alloys are irreplaceable in aerospace, biomedical and marine industries due to their low density, high specific strength and excellent biocompatibility. Conventional manufacturing methods suffer from low material utilization and difficulty in fabricating complex components, while additive manufacturing (AM) realizes near-net-shape forming of customized structures but introduces unique non-equilibrium microstructures and defects, which significantly alter the corrosion behavior and limit the long-term service reliability of additively manufactured (AMed) titanium alloys. This work systematically analyzes the corrosion behavior of titanium alloys fabricated by four mainstream AM processes: LPBF (laser powder bed fusion)/SLM (selective laser melting), EBM (electron beam melting), DED (directed energy deposition) and WAAM (wire arc additive manufacturing). It quantitatively summarizes the key electrochemical parameters and discusses the regulatory effects of matrix composition, post-treatment and service environment on their corrosion behaviors. The universal corrosion mechanisms—namely, passive film breakdown, micro-galvanic corrosion, and defect-induced localized corrosion—as well as process-specific corrosion mechanisms inherent to AMed titanium alloys are systematically elucidated. This study offers theoretical foundations for optimizing corrosion resistance and ensuring the reliable engineering implementation of AMed titanium alloys.