Physical Vapor Deposition of Carbon-Doped TiAlTaZrNb High-Entropy Alloy Coatings for Corrosion Protection of H13 Steel

High-entropy alloy (HEA) coatings exhibit enhanced chemical stability when doped with carbon, primarily due to the strong bonding between carbon and transition metals. Typical transition metals used in these coatings include Cr, Fe, Co, Ni, Cu, Ti, V, W, Nb, Ta, and Zr. Owing to their excellent chemical stability, HEA coatings are widely employed to protect component surfaces operating in highly corrosive environments. Against this backdrop, the present study investigates the effect of carbon doping introduced via methane gas flow during the physical vapor deposition of TiAlTaZrNb HEA coatings on corrosion resistance. The morphology and structure of the coatings were analyzed by field emission scanning electron microscopy, X-ray diffraction, and Raman spectroscopy. Corrosion protection and coating resistance were assessed through potentiodynamic polarization and electrochemical impedance spectroscopy. While increasing the methane flow resulted in an approximately 34% reduction in coating thickness, the overall coating resistance increased by one order of magnitude, reaching a maximum at a methane flow rate of 9 sccm, corresponding to the carbon solubility limit. This improvement was evidenced by a decrease in the corrosion rate from 8.02 × 10−2 mm y−1 for the uncoated H13 steel to 8.00 × 10−4 mm y−1 for the HEA-coated samples. However, at higher methane flow rates, carbon precipitation and the formation of parallel microcracks contributed to an increase in corrosion rate.