Optimized Electroless Deposition of Co on Activated WC Powders for WC-Co Cemented Carbides with Enhanced Mechanical Performance

High-quality WC-Co composite powder is the prerequisite for achieving cemented carbides with superior mechanical properties. However, achieving homogeneous Co distribution on WC particles remains challenging due to the limited surface activity of WC and the high cost associated with noble-metal activation methods. Therefore, this study employed an electroless plating method based on non-noble-metal activation to prepare Co- coated WC composite powders and to clarify the effects of plating parameters on coating behavior, microstructure evolution, and mechanical properties of WC-Co cemented carbides. Results indicate that when plated with a lower reducing-agent concentration (15 g/L) or a lower temperature (70 °C), insufficient Co coating causes poor fracture toughness of the cemented carbides. Increasing the reducing-agent concentration to 25 g/L or the plating temperature to 80 °C promotes a more uniform Co distribution on WC particles, which suppresses WC grain coalescence during sintering. Under the optimized reducing-agent concentration of 25 g/L, the obtained WC-Co cemented carbide exhibits a homogeneous microstructure with an average WC grain size of 0.91 μm, a Vickers hardness of 2054.5 HV30, and a fracture toughness of 11.39 MPa·m1/2. Excessive reducing-agent concentration or plating temperature deteriorates the Co coating uniformity, promoting Co aggregation and grain coarsening of the cemented carbides. This work demonstrates that precise control of electroless plating parameters enables the fabrication of high-quality WC-Co composite powders, providing a practical route for tailoring microstructure and optimizing mechanical performance of the cemented carbides.