NaOH-Induced Changes in Physical, Mechanical, and Chemical Properties of Artificial Archaeological Wood

Waterlogged archaeological wood represents a unique cultural heritage but is highly susceptible to physical and chemical degradation, which complicates conservation and restoration. This study aimed to prepare artificial archaeological Cunninghamia lanceolata wood using NaOH vacuum impregnation and systematically evaluate the effects of NaOH concentration and treatment cycles as two treatment variables on wood degradation. Untreated heartwood specimens were treated with 5%, 10%, 20%, and 30% NaOH solutions for 2, 4, and 6 cycles. The NaOH treatment first induced chemical and structural deterioration, including selective degradation of hemicelluloses, changes in cellulose crystallinity, and progressive damage to the wood cell-wall structure. XRD analysis revealed a significant reduction in cellulose crystallinity from 35.96% to 10.11%, while FTIR confirmed the degradation of hemicelluloses and the relative enrichment of lignin-related structures. SEM observations further showed severe cell-wall erosion, lumen deformation, and local collapse, indicating that alkali treatment effectively reproduced typical microstructural features of degraded waterlogged wood. These chemical and microstructural changes subsequently led to marked changes in physical and mechanical properties. Mass loss increased with NaOH concentration and cycle number, while basic density decreased and maximum water content increased, indicating enhanced deterioration and water-holding capacity. Treated specimens also exhibited increased swelling and shrinkage rates and a substantial reduction in longitudinal compressive strength, with the most pronounced deterioration occurring under higher NaOH concentrations and repeated cycles. The study demonstrates that NaOH treatment can reproducibly simulate the physical, chemical, and microstructural characteristics of waterlogged archaeological wood, providing a reliable experimental model for studying wood degradation mechanisms and supporting conservation strategies.