Interfacial Adhesion Mechanism of Anionic Polyelectrolyte Brushes Induced by Oppositely Charged Macromolecular Counterions

Abstract

Polyelectrolyte brushes are widely used as model systems for investigating electrostatic interactions at soft interfaces and to achieve exceptional lubrication properties. Previous studies have primarily focused on their behavior in the presence of multivalent counterions, which induce brush collapse, ionic crosslinking, and pronounced changes in interfacial structures. However, interactions between polyelectrolyte brushes and oppositely charged macromolecular counterions, such as polycations, remain poorly understood. Here, we prepare well-defined polystyrene sulfonate (PSS) brushes fabricated via surface-initiated grafting and employ surface forces apparatus measurements to investigate their interactions with oppositely charged polycations. In contrast to multivalent ions, polycations do not induce noticeable brush collapse, but instead generate significant adhesion between symmetric PSS brush layers. This adhesion increases with both contact time and applied load, eventually reaching a steady plateau, indicating that the interaction is governed not simply by electrostatic screening but by the gradual formation of polycation-mediated bridging under confinement. Furthermore, the introduction of monovalent Na+ ions disrupts the adhesive interaction even at very low concentrations, suggesting that the bridging function of the adsorbed polycation is highly sensitive to competitive ionic screening. In comparison, measurements with trivalent counterions reveal the expected brush collapse behavior but minimal dependence of adhesion on contact time, highlighting a clear mechanistic distinction from the polymeric counterion case. Collectively, these results demonstrate that molecular size, configurational restriction, and confinement-induced rearrangement, rather than charge valency alone, govern the interaction behavior of macromolecular counterions at brush interfaces. This work provides new insight into the molecular origins of adhesion and the regulation of interfacial interactions in charged polymer brush systems.