Establishing the Stability of Cross-Linked Poly(ethylene oxide) Blended with Poly(pentyl malonate) against Lithium Metal Anodes

Abstract

This work focuses on an electrolyte obtained by infusing linear poly(pentyl malonate) (PPM) chains into cross-linked poly(ethylene oxide) (PEO). A lithium salt is added to enable ion transport. Obtaining this electrolyte is only possible because PPM is miscible with PEO irrespective of salt concentration. The properties of this electrolyte are compared against two benchmarks: an electrolyte obtained by infusing linear PEO into cross-linked PEO and cross-linked PEO with no added linear polymer. Measurements of storage moduli and ion transport efficacies are found to be similar across the three electrolytes, suggesting similar stability behavior against lithium metal anodes, based on current theoretical models. Instead, the PPM infused electrolyte outperforms the other two electrolytes. In the cycling tests, the current supported by the PPM infused electrolyte was a factor of 20 higher than that of the PEO infused electrolyte and a factor of 4 higher than that of the cross-linked PEO electrolyte. In the unidirectional plating experiments, the other two electrolytes fail after about 4 h or less, while the PPM containing electrolyte did not fail during the 140 h testing period. Insight into the nature of failure modes was obtained using synchrotron hard X-ray microtomography.