Enhanced Phosphate Capture by Thermally Modified Calcium Aluminate Decahydrate: Optimization, Performance and Mechanism

Adsorption is a promising technology for phosphate removal to alleviate eutrophication. In this study, thermally modified calcium aluminate decahydrate (TCAH) was prepared via low-temperature thermal treatment of calcium aluminate decahydrate (CAH10) to develop a cost-effective and high-performance phosphate adsorbent. The optimal modification temperature was determined to be 120 °C, which reduced the crystallinity of CAH10, enhanced its porosity, and induced the formation of amorphous calcium aluminate phases. Batch adsorption experiments showed that TCAH exhibited a maximum adsorption capacity of 199.80 mg P/g at 25 °C. The adsorption kinetics followed the pseudo-second-order model, while the adsorption isotherms were well fitted by the Redlich–Peterson model. TCAH maintained high removal efficiency over a wide pH range of 3.0–11.0 and showed high selectivity against common coexisting anions. Characterizations using SEM-EDS, XRD, FTIR and XPS suggested that phosphate removal by TCAH was dominated by synergistic amorphous precipitation and inner-sphere complexation. In tests with real phosphorus-releasing liquor derived from excess sludge, TCAH achieved nearly complete phosphate removal at a dosage of 5 g/L within 6 h. Owing to its readily available raw materials, low preparation temperature, and outstanding phosphate capture performance, TCAH is a promising candidate for efficient phosphate capture and recovery from wastewater.