Effect of Prolonged Austempering Within Transformation Stasis on the Microstructural Evolution and Mechanical Behavior of Nanostructured Bainitic Steel

This study examines the evolution of microstructure, the metastability of retained austenite (RA), and the corresponding mechanical behavior exhibited by a nanostructured bainitic bearing steel subjected to prolonged austempering within a transformation stasis regime. The results indicate that following the completion of nanostructured bainitic formation at 300 °C for 3 h, a prolonged austempering time does not alter the microstructure, but reduces the dislocation density in BF while increasing the carbon content in RA. For the 4 h and 6 h specimens, a reduction in the overall RA mechanical stability is observed, accompanied by different transformation rates of stress-induced martensite during tensile deformation. This behavior is largely due to the weakened constraint effect of the BF matrix and the evolution of a carbon concentration gradient within the RA. During the transformation stasis, prolonged austempering elevates the yield strength while maintaining an unchanged ultimate tensile strength, albeit with a marginal reduction in microhardness. Relative to the baseline elongation recorded for the 3 h specimen, both the 4 h and 6 h specimens exhibit enhanced ductility, with the 4 h specimen yielding a peak value of 16.8%, which is 1.66 times that of the 3 h specimen. This improvement stems largely from the greater RA volume fraction that transforms into stress-induced martensite in the 4 h specimen, as well as its continuous and stable transformation rate during tensile deformation. Therefore, it can be concluded that an appropriately prolonged austempering time within nanostructured bainitic transformation stasis is essential for optimizing mechanical performance. This study provides a low-cost, energy-saving isothermal heat treatment technical scheme for mass industrial production of high-performance bearing steel.