Comparative Short-Term Electrochemical and Surface Characterization of Biodegradable Mg–Ca–Sr Alloys with Different Strontium Contents

Biodegradable Mg–Ca–Sr alloys are promising candidates for temporary implant applications, but their degradation behavior is strongly influenced by alloy composition and electrolyte chemistry. This comparative short-term study investigated how increasing the Sr content from 0.5 to 1.5 wt.% influences the electrochemical response and surface characteristics of cast Mg–0.5Ca–xSr alloys in 0.9% NaCl and calcium- and magnesium-free Dulbecco’s phosphate-buffered saline (DPBS). Potentiodynamic polarization, electrochemical impedance spectroscopy, scanning electron microscopy, quantitative image analysis, and energy-dispersive X-ray spectroscopy were used. Increasing the Sr content reduced the corrosion-current density from 0.0110 to 0.0039 mA/cm2 in NaCl and from 0.297 to 0.169 mA/cm2 in DPBS, while the corresponding calculated corrosion rates decreased from 2.51 to 0.886 mm/year and from 6.66 to 3.79 mm/year, respectively. Replicated EIS measurements of both alloys showed that Mg–0.5Ca–1.5Sr exhibited higher charge-transfer resistance than Mg–0.5Ca–0.5Sr in both NaCl (253 ± 15 versus 184 ± 14 Ω·cm2) and DPBS (853 ± 48 versus 615 ± 42 Ω·cm2). NaCl-exposed surfaces showed more porous and discontinuous deposits and a greater number of visible pit-like defects, whereas DPBS produced comparatively continuous P-containing deposits. Overall, increasing the Sr content to 1.5 wt.% was associated with lower polarization-derived global corrosion kinetics and a more resistive interfacial response, whereas electrolyte composition strongly influenced both interfacial impedance and surface-deposit morphology. These findings represent comparative short-term electrochemical and surface-characterization data obtained at 23 ± 1 °C and should not be interpreted as measures of long-term physiological degradation or in vivo performance.